Title: Obtenção de pós e filmes finos do sistema SrTiO3:Nd
Other Titles: Obtention of Powders and Thin Films of the SrTiO3:Nd System
???metadata.dc.creator???: Silva, Marcia Rejane Santos da
???metadata.dc.contributor.advisor1???: Santos, Ieda Maria Garcia dos
First advisor-co: Souza, Antonio Gouveia de
???metadata.dc.description.resumo???: SrTiO3 é um composto de estrutura perovskita comumente encontrado na fase cúbica. Este trabalho reporta a síntese de pós e filmes finos deste composto na sua forma pura e dopada com Nd3+ em substituição a Ti4+ ou Sr2+ nas estequiometrias SrTi1-xNdxO3 (x = 0,00; 0,01; 0,02; 0,04) e Sr0,99Nd0,01TiO3. Os pós foram sintetizados pelo método dos precursores poliméricos. Os filmes finos foram preparados pelo método de deposição de solução química (CSD) utilizando a técnica spin coating e pelo método de deposição por laser pulsado (PLD), sendo depositados em substratos de LaAlO3 (100), MgO (100), SrTiO3 (100), Al2O3-R, e SiO2. As propriedades estruturais e óticas desses materiais foram avaliadas por espectroscopia de infravermelho, espectroscopia UV-Vis, espectroscopia de emissão fotoluminescente, espectroscopia micro Raman e difração de raios-X (DRX). Refinamento Rietveld dos dados de DRX foi realizado para algumas amostras em pó. Além disso, a propriedade fotocatalítica foi estudada frente à degradação de corantes têxteis. A coexistência das fases cúbica e tetragonal para os pós de SrTiO3 foi confirmada, já na temperatura de 550 ºC e foi verificado para as amostras dopadas (700 ºC) que o sítio de ocupação do Nd3+ influenciou na quantidade dessas fases. Esse resultado teve influência direta na propriedade fotoluminescente observada. Os materiais emitiram principalmente na região do amarelo, mas com o aumento da temperatura essa região se deslocou para o verde (maior energia) indicando a organização do sistema. Os filmes finos depositados sobre o substrato de LaAlO3 mostraram crescimento epitaxial de alta qualidade por CSD e de qualidade muita alta por PLD. Sobre MgO a dopagem influenciou na orientação dos filmes. Os filmes depositados em Al2O3-R, e SiO2 foram policristalinos. A eficiência de degradação fotocatalítica foi similar entre pós e filmes puros, sendo aumentada com 4 % de Nd3+ nos filmes depositados por PLD.
Abstract: SrTiO3 is a compound with perovskite structure usually found with cubic phase. This works reports the synthesis of powders and thin films of the undoped and Nd3+ doped SrTiO3, replacing Ti4+ or Sr2+ with the stoichiometries SrTi1-xNdxO3 (x = 0.00; 0.01; 0.02; 0.04) and Sr0.99Nd0.01TiO3. The powders were synthesized by the polymeric precursor method. The thin films were prepared by chemical solution deposition (CSD) using the spin coating technique and by pulsed laser deposition (PLD), being deposited on LaAlO3 (100), MgO (100), SrTiO3 (100), Al2O3-R, and SiO2. The structural and optical properties of these materials were evaluated by infrared spectroscopy, UV-vis spectroscopy, photoluminescent emission, micro Raman spectroscopy and X-ray diffraction (XRD) Rietveld refinement of the XRD patterns was realized for powder samples. Moreover the photocatalytic property was evaluated in the degradation of textile dyes. The coexistence of the cubic and tetragonal phases for SrTiO3 powders was confirmed after calcinations at 550 oC. For doped samples calcined at 700 oC, it was observed that the sites occupied by Nd3+ influenced in the amount of these phases, leading to a direct influence in the photoluminescent emission. Emission in the yellow region was observed, while temperature increase lead to a shift to the green region, with higher energy indicating that short range ordering occurred. Thin films deposited on LaAlO3 substrate showed high quality epitaxial growth by CSD and a very high quality by PLD. On MgO doping changed the film orientation. For deposition on Al2O3-R and SiO2, polycrystalline films were obtained. Photocatalytic degradation efficiency was similar in powders and undoped films, increasing for films doped with 4 % of Nd3+ when synthesis was done by PLD. Key words:
Keywords: SrTiO3:Nd
Cúbico
Tetragonal
Neodímio fotoluminescência
Filme fino
Deposição por laser pulsado
Deposição de solução química
SrTiO3:Nd
Cubic
Tetragonal
Neodymium
Photoluminescence
Thin film
???metadata.dc.subject.cnpq???: CIENCIAS EXATAS E DA TERRA::QUIMICA
Language: por
???metadata.dc.publisher.country???: BR
Publisher: Universidade Federal da Paraí­ba
???metadata.dc.publisher.initials???: UFPB
???metadata.dc.publisher.department???: Química
???metadata.dc.publisher.program???: Programa de Pós-Graduação em Química
Citation: SILVA, Marcia Rejane Santos da. Obtenção de pós e filmes finos do sistema SrTiO3:Nd. 2010. 220 f. Tese (Doutorado em Química) - Universidade Federal da Paraí­ba, João Pessoa, 2010.
???metadata.dc.rights???: Acesso Aberto
URI: http://tede.biblioteca.ufpb.br:8080/handle/tede/7191
Issue Date: 15-Dec-2010
Appears in Collections:Centro de Ciências Exatas e da Natureza (CCEN) - Programa de Pós-Graduação em Química

Files in This Item:
File Description SizeFormat 
arquivototal.pdf7.93 MBAdobe PDFThumbnail

Download/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.